Jh15780 77% High Zinc Inorganic Silicate Coating for Steel Structure Paint

• Usage: Anticorrosive Paint
• Color: Black
• Appearance: Liquid
• Method: Spray
• Components: Film Forming Matter
• Main Raw Material: Epoxy
• Model NO.: JH15780
• Level: Primer
• Certification: ISO14001, CCC, RoHS, ISO9001
• Substrate: Iron
• Expiration Date: 3 years
• Formation Mechanism: Non Conversion Type
• Packaging: Iron Drum
• Transport Package: Towing Raft
• Specification: 20kg/barrel
• Trademark: Spnal
• Origin: China
• Production Capacity: 50000tons / Year

Product Description

JH15780 High zinc inorganic silicate coating (Zinc 77%)
Description
This product is a solvent-based, two-component, self-curing inorganic zinc silicate coating with moderate zinc content. Airless spraying is used.
Recommended use
As a universal anti-corrosion primer in paint systems, it provides long-term protection for steel exposed to moderate to severe corrosion. According to SSPC-Paint 20 Type 1 Level 2.
Applications: Steel structure paint, coating on Bridges and structures, covering ports and docks
specification

Component weight ratio	4.2:5.8
Volume ratio of non-volatile material	62±2%
Specific gravity	2.3 kg/l
Refer to dry film thickness	50 micron
Flash point	14ºC
VOC content in mixed products	471 g/l
Application period 20ºC	4 hours
Theoretical covering power	12 m2 / L 50 microns
Film forming time	16 hours
Shelf life	12 months