Jh15700 85% High Zinc Inorganic Silicate Coating for Steel Structure Paint

• Usage: Anticorrosive Paint
• Color: Black
• Appearance: Liquid
• Method: Spray
• Components: Film Forming Matter
• Main Raw Material: Epoxy
• Model NO.: JH15700
• Level: Primer
• Certification: ISO14001, CCC, RoHS, ISO9001
• Substrate: Iron
• Expiration Date: 3 years
• Formation Mechanism: Non Conversion Type
• Packaging: Iron Drum
• Transport Package: Towing Raft
• Specification: 20kg/barrel
• Trademark: Spnal
• Origin: China
• Production Capacity: 50000tons / Year

Product Description

JH15700 High zinc inorganic silicate coating (Zinc 85%)

Description
The product is a self-curing, solvent-based, high zinc inorganic silicate primer with excellent weather resistance and wear resistance. Provides excellent current protection against local mechanical damage. Excellent chemical resistance in the pH range 6-9. The product meets the formulation requirements of SSPC Paint 20, Type I, Level 1 and ISO 12944 Part 5, 2018.
Recommended use
Recommended as a general purpose, heavy duty, rust resistant primer for new construction and renovation projects. Suitable for structural steel and piping. Recommended for use in a variety of harsh atmospheric environments up to the extreme (at sea). Can be used as a single composite coating to provide long-term protection for steel exposed to moderate to severe corrosive environments and wear. Also suitable for storage tank lining.
Applications: steel structure paint, coating on Bridges and structures, Marine covering, covering ports and docks
specification

Component weight ratio	3.4:6.6
Volume ratio of non-volatile material	64±2%
Specific gravity	2.5 kg/l
Refer to dry film thickness	50 micron
Flash point	18 ºC
VOC content in mixed products	474 g/l
Application period 20ºC	4 hours
Theoretical covering power	13 m2 / L 50 microns
Film forming time	24 hours
Shelf life	6 months